In this paper, a multifunctional nanofibrous cellulose acetate/gelatin/Zataria multiflora-nanoemulsion (CA/Gel/ZM-nano) wound dressing was fabricated, in which nanoemulsion of a natural active antibacterial plant, by the scientific name of Zataria multiflora (ZM) was loaded into the nanofibrous mat. To fabricate the wound dressing, different weight ratios of CA/Gel (100, 0, 75, 25, 50, 50 and 25, 75) were selected, and solutions with concentrations of 16, 15, 14 and 12% w/v were prepared for each ratio, respectively to achieve smooth and uniformfibers by electrospinning. In vitro and in vivo analysis was taken for the samples. Nanofibrous mats with a lower ratio of CA/Gel and incorporated with ZM-nano promoted the adhesion and proliferation of L929 fibroblast cells significantly. Also, by lowering the ratio of CA/Gel, nanoemulsion drug-loading into nanofibers increased considerably, as the amount of ZM-nano loaded into CA/Gel = 50:50 was found to be 2.4-fold higher than CA/Gel = 100:0. Moreover, the rat model experiment in our study revealed that the nanofibrous samples incorporated with nanoemulsion drug (ZM-nano) accelerated the wound healing process so that the relative wound area for the nanoemulsion-loaded dressings was much smaller than the other samples after 22 days. Therefore, this multifunctional CA/Gel/ZM-nano wound dressing could be a promising and potential candidate for wound healing applications. (C) 2020 Elsevier B.V. All rights reserved.