Bicomponent composite fibers, due to their unique versatility, have attracted great attention in many fields, such as filtration, energy, and bioengineering. Herein, we efficiently fabricated polyvinylidene fluoride /polyimide (PVDF /PI) side-by-side bicomponent nanofibers based on electrospinning, which resulted in the synergism between PVDF and PI, and eventually obtained the effect of 1 + 1 > 2. Scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FTIR) were used to characterize the morphology and chemical structure of nanofibers, indicating that a large number of side-by-side nanofibers were successfully prepared. Further, the thermal stability, mechanical strength, and filtration properties of PVDF /PI were carefully investigated. The results revealed that the bicomponent nanofibers possessed both good mechanical strength and remarkable thermal stability. Moreover, the mechanical properties of PVDF/ PI were strengthened by more than twice after the heat treatment (7.28 MPa at 25 degrees C, 15.49 MPa at 230 degrees C). Simultaneously, after the heat treatment at 230 degrees C for 30 min, the filtration efficiency of PVDF /PI membrane was maintained at about 95.45 +/- 1.09%, and the pressure drop was relatively low. Therefore, the prepared PVDF /PI side-by-side bicomponent nanofibers have a favorable prospect of application in the field of medium- and high-temperature filtration, which further expands the application range of electrospun fiber membranes.