Characterization of PVDF/PU fibers prepared by electrospinning
2019/11/27 21:42:24 admin
The 23 wt% polyvinylidene fluoride (PVDF)/15 wt% polyurethane (PU) fibers were electrospun using the conjugated nozzle at a flow rate of 1.0 mL/h and an electric field of 1 kV/cm. The formation of beta crystal phase in the PVDF and the PVDF/PU fibers was confirmed by Fourier transform infrared spectroscopy. After electrospinning, the asspun fibers were immersed in a boiling water and then dried at 100 degrees C in a convection oven to make a crimp phenomenon. The crimps with a diameter of 2.0 +/- 0.08 mu m were observed for the PVDF/PU fibers after hydrothermal treatment without sacrificing the extent of beta crystal phase. All the PU, PVDF and PVDF/PU fibers exhibited average cell viability of more than 98 %. The cell proliferation results suggested that L-929 cells adhered well to the PU, PVDF and PVDF/PU fibers and proliferated continuously with increasing time, indicating that the PVDF/PU fibers are highly applicable to the biomedical applications.
相关推荐
暂无相关推荐
网友评论 请遵循相关法律法规,理性发言
回复
查看更多回复

分享