A novel approach, continuous needleless electrospinning from the tips of magnetization-induced self-assembling PVA/ferrofluid cone array, was proposed to prepare magnetic nanofibers. A PVA/ferrofluid was synthesized, the needleless electrospinning process was observed, and the morphology and magnetic properties of magnetic nanofibers were investigated. The results showed that the PVA/ferrofluid could remain stable and homogeneous for 21 days under the magnetic field gradient (2.2 mT/mm). "Taylor cone" array of PVA/ferrofluid was self-assembled under both the magnetic and electric fields. As the electric voltage reached 25 kV, the jets were emitted from the "Taylor cone" array, resulting in needleless electrospinning of magnetic nanofibers. Magnetic nanofibers were homogeneous and continuous with an average diameter of 73.6 nm. Magnetic nanofibers showed a good magnetic response property and relatively high saturated magnetization (1.71 emu/g), which is expected to be applied in the biomedical field. (C) 2017 Elsevier B.V. All rights reserved.