Excitation dependent recombination studies on SnO2/TiO2 electrospun nanofibers
2019/11/27 21:40:52
admin
Poly(vinyl acetate) (PVAc)/TiO2 nanofibers, PVAc/SnO2 nanoribbons and PVAc/SnO2-TiO2 nanoribbons were produced via electrospinning. TiO2 nanofibers and SnO2 nanoribbons were obtained by removal of the polymeric matrix (PVAc) after calcination at 450 degrees C. Interestingly, PVAc/SnO2-TiO2 nanoribbons were transformed into SnO2-TiO2 nanofibers after calcination under the similar conditions. Fiber morphology and elemental mapping confirmed through SEM and TEM microscope techniques respectively. The X-ray diffraction measurements suggested the presence of anatase TiO2 and rutile SnO2 and both were present in the SnO2-TiO2 mixed system. Systematic photoluminescence studies were performed on the electrospun nanostructures at different excitation wavelengths (lambda(ex1) = 325, lambda(ex2) = 330, lambda(ex3) = 350, lambda(ex4) = 397 and lambda(ex5) = 540 nm). We emphasize that the defects in the SnO2-TiO2 based on the defect levels present in TiO2 and SnO2 and anticipate that these defect levels may have great potential in understanding and characterizing various semiconducting nanostructures.

0
网友评论
请遵循相关法律法规,理性发言
查看更多回复