The preparation of electrospun polymer Microfibers with nitric oxide (NO)-release capabilities is described. Polymer solutions containing disodium 1-[2-(carboxylato)-pyrrolidin-1-yl]diazen-1-ium-1,2-diolate (PROLI/NO), a low-molecular-weight NO donor, were electrospun to generate fibers ranging from 100-3000 nm in diameter capable of releasing NO upon immersion in aqueous solutions under physiological conditions (pH 7.4, 37 degrees C), with kinetics depending on polymer composition and fiber diameter. The NO release half-life for PROLI/NO-doped electrospun fibers was 2-200 times longer than that of PROLI/NO alone. The influence of polymer concentration, applied voltage, capillary diameter, solution conductivity, flow rate, and additives on fiber properties are reported and discussed with respect to potential applications.