Scaffolds and their features play a central role in tissue engineering; so this study is based on the production of a series of electrospun PHB/Chitosan/nBG nanocomposite scaffolds with 9 wt% polyhydroxybutyrate, 10, 15 and 20 wt% chitosan and 7.5, 10 and 15 wt% nanobioglass (nBG). Electrospinning process was performed with optimal conditions of spinning machine including voltage of 16 kV, syringe-collector spacing of 16 cm, and output rate of 1 mu l per hour. The developed phases and the formation of chemical bonds between ceramic and polymer bands were studied through XRD and FTIR analyses. The FE-SEM and TEM analyses showed uniform morphology of nanofibers and dispersion of bioglass nanoparticles in the fiber structure. The presence of 10 wt% bioglass nanoparticles and 15 wt% chitosan increased the tensile strength of fibers to 3.42 MPa, which was about four times greater than strength of control sample (pure PHB). The developed fibers were kept 28 days in SBF solution and 60 days in PBS solution to assess their bioactivity and biodegradability. The results showed that the presence of bioglass nanoparticles leads to a dramatic increase in absorption of calcium and phosphorus ions and weight loss of scaffold. The developed scaffold can be used for bone and teeth tissue engineering applications.