Although polyacrylonitrile (PAN) has excellent properties as a precursor of carbon fibre, octa-amic polyhedral oligomeric silsesquioxane (POSS) nanoparticles which are hybrid organic-inorganic materials can be incorporated into PAN to tune up the properties such as the mechanical strength, thermal conductivity, and electronic conductivity for a broad range of potential applications. In this work, PAN with POSS of 1, 3, and 5wt % based on acrylonitrile weight was prepared by solution polymerisation. The synthesised product was dissolved in dimethyl sulphoxide, followed by electrospinning. After electrospinning, the nanofibrous mats were stabilised at 250 degrees C for 1h. The diameter of resulting PAN/POSS nanofibrous mats were less than 1m, as confirmed by SEM analysis. The effect of POSS on PAN/POSS nanofibrous mats was studied by SEM, universal testing machine, contact angle measurement, Fourier transform infrared spectroscopy, wide angle X-ray diffraction, differential scanning calorimetry, and thermogravimetric analysis. The usefulness of the PAN/POSS nanofibre composites was realised from the improved electrical, thermal, mechanical, and wetting properties compared to pure PAN.