The purpose of this work was to investigate the possibility for the preparation of new poly(3-hydroxybutyrate) (PHB)/poly(ethylene glycol) (PEG)-based fibrous materials containing natural phenolic compound caffeic acid (CA) of diverse architectures, as well as to study the impact of the fiber composition on the in vitro CA release profile and on the biological properties of the fibrous materials. The application of the one-pot electrospinning enabled the fabrication of nanofibrous materials from PHB and PEG loaded with the CA. Materials with targeted design were obtained by coating with polyelectrolyte complex of alginate (Alg) and N,N,N-trimethylchitosan (TMCh). Three different processing paths were used to obtain coated mats: (i) with CA incorporated in the PHB/PEG core; (ii) with CA embedded in the Alg layer; and (iii) with CA included in the TMCh layer. The in vitro release of CA was modulated by controlling the composition and the architecture of the nanofibrous mats. The performed microbiological screening and MIT cell viability studies revealed that in contrast to the bare mats, the CA-containing nanofibrous materials were effective in suppressing the growth of the Gram-positive bacteria Staphylococcus aureus and the Gram-negative bacteria Escherichia coli and displayed good cytotoxicity against human cervical HeLa tumor cells. In addition, the proliferation of murine spleen lymphocytes and peritoneal macrophages was increased by the prepared CA-containing nanofibrous materials. The obtained materials are promising for antibacterial wound dressing applications as well as for application in local treatment of cervical tumors. (C) 2016 Elsevier B.V. All rights reserved.