High mechanical performance materials at high temperature are highly desired for the materials used in high temperature industries. This study reports the aligned electrospun polyimide nanofiber belt (A-PI-NFB) fabricated from the electrospinning followed with imidization. The A-PI-NFB showed increased mechanical and thermal mechanical properties as increasing the imidization temperature. At room temperature, the A-PI-NFB imidized at 450 degrees C (A-PI-NFB-450) had the highest tensile strength (689 MPa) and E modulus (13.2 GPa). The thermomechanical analysis (TMA) and dynamic mechanical analysis (DMA) showed that A-PI-NFB-450 possessed 80% tensile strength and 90% modulus when heated at 300 and 350 degrees C in N-2, respectively. These excellent properties made A-PI-NFB good candidates for use in high temperature filtration, protective clothes etc. (C) 2014 Elsevier B.V. All rights reserved.