Fabrication of GdBaCo2O5+delta cathode using electrospun composite nanofibers and its improved electrochemical performance
2019/11/27 21:34:25 admin
GdBaCo2O5+delta (GBCO)/poly (vinyl pyrrolidone) (PVP) composite nanofibers were prepared by electrospinning. Structural and morphological evolution of the GBCO/PVP fibers under calcinations at various temperatures was studied. Using 600 degrees C pre-calcined GBCO/PVP composite nanofibers, pure phase GBCO cathode with homogeneous network structure was easily fabricated on Ce0.9Gd0.1O1.95 (GDC) electrolyte. The as-prepared GBCO cathode was characterized by electrochemical impedance spectra (EIS) measurements based on a GBCO/GDC/GBCO symmetric cell. Its electrochemical performance was compared with the cathode prepared with the GBCO powders synthesized with sol-gel method. The GBCO cathode fabricated using GBCO/PVP composite fibers had area specific resistances (ASRs) of 0.53 Omega cm(2) at 600 degrees C, 0.22 Omega cm(2) at 650 degrees C, 0.10 Omega cm(2) at 700 degrees C and 0.043 Omega cm(2) at 750 degrees C respectively, which are lower than ASR results of the GBCO cathode prepared with powders. The results have demonstrated that the GBCO cathode fabricated using electrospun composite nanofibers has significantly enhanced electrochemical activities for oxygen reduction reaction, and it can serve as a promising cathode material for intermediate- temperature solid oxide fuel cell. (c) 2013 Elsevier B.V. All rights reserved.
相关推荐
暂无相关推荐
网友评论 请遵循相关法律法规,理性发言
回复
查看更多回复

分享