Electrospinning of polycarbonate (PC)/chloroform solution with quaternary ammonium salt (benzyl triethylammonium chloride, BTEAC) was investigated to develop antimicrobial nanofibrous membranes for ultrafiltration. With BTEAC additive, ultrafine PC fibers were continuously generated and densely mounted without the blockage of spinning tip on electrospinning. When small amounts of BTEAC were added to the PC solution, the average diameter was also decreased from several micrometers to submicron range. It was found that the conductivity of the PC solution was a major parameter affecting the morphology and diameter of the electrospun PC fibers as well as the electrospinnability of PC. The nanofibrous membranes electrospun from the PC solution with BTEAC exhibited better excellent antimicrobial activity than those prepared without BTEAC. The PC nanofibrous filter shows a good filtration efficiency to satisfy the criterion of HEPA filter, and the pressure drop of the PC filters are within the normal range. Therefore, PC nanofibrous membrane showed a great potential as a candidate for ultrafiltration, compared to a commercial HEPA filter. (c) 2007 Elsevier Ltd. All rights reserved.