We show that the combination of direct membrane deposition with proton conductive nanofiber reinforcement yields highly durable and high power density fuel cells. Sulfonated poly(ether ketone) (SPEK) was directly electrospun onto gas diffusion electrodes and then filled with Nafion by inkjet-printing resulting in a 12 mu m thin membrane. The ionic membrane resistance (30 m Omega*cm(2)) was well below that of a directly deposited membrane reinforced with chemically inert (PVDF-HFP) nanofibers (47 m Omega*cm(2)) of comparable thickness. The power density of the fuel cell with SPEK reinforced membrane (2.04 W/cm(2)) is 30% higher than that of the PVDF-HFP reinforced reference sample (1.57 W/cm(2)). During humidity cycling and open circuit voltage (OCV) hold, the SPEK reinforced Nafion membrane showed no measurable degradation in terms of H-2 crossover current density, thus fulfilling the target of 2 mA/cm(2) of the DOE after degradation. The chemical accelerated stress test (100 h OCV hold at 90 degrees C, 30% RH, H-2/air, 50/50 kPa) revealed a degradation rate of about 0.8 mV/h for the fuel cell with SPEK reinforced membrane, compared to 1.0 mV/h for the PVDF-HFP reinforced membrane. (C) 2017 Elsevier B.V. All rights reserved.