This work reports the precise diameter control of electrospun yttria-stabilized zirconia (YSZ) nanofibers from 200 to 900 nm after calcination. Fabricated YSZ nanofibers showed porous nanocrystalline structures with high aspect ratios of more than 500: 1 and high surface-to-volume ratios with a specific surface area of 43.32 m(2)/g. The diameter of the YSZ nanofibers increased with the viscosity of the precursor solution, which was controlled by the concentrations of either polymers (polyacrylonitrile) or ceramic precursors (YSZ). We present a modified correlation between the diameter of a nanofiber and the synthetic conditions, as the observed behavior for calcined ceramic nanofibers deviated from the expected behavior. Our results demonstrate a modified but simple approach to fabricate ceramic nanofibers with desired diameters, providing a new design guideline for many electrochemical applications.