Unidirectionally and orthogonally aligned thermoplastic polyurethane (TPU) nanofibers were electrospun using a custom-built electrospinning device. The unidirectionally aligned fibers were collected using two parallel copper plates, and the orthogonally aligned fibers were collected using two orthogonal sets of parallel copper plates with alternate negative connections. Carbon nanotubes (CNT) and polyacrylic acid (PAA) were added to modify the polymer solution. It was found that both CNT and PAA were capable of increasing solution conductivity. The TPU/PAA fiber showed the highest degree of fiber orientation with more than 90% of the fibers having an orientation angle between -10 degrees and 10 degrees for unidirectionally aligned fibers, and for orthogonally aligned fibers, the orientation angle of 50% fibers located between -10 degrees and 10 degrees and 48% fibers located between 80 degrees and 100 degrees. Viability assessment of 3T3 fibroblasts cultured on TPU/PAA fibers suggested that the material was cytocompatible. The cells' orientation and migration direction closely matched the fibers' orientation. The cell migration velocity and distance were both enhanced with the guidance of fibers compared with cells cultured on random fibers and common tissue culture plastic. Controlling cell migration velocity and directionality may provide ways to influence differentiation and gene expression and systems that would allow further exploration of wound repair and metastatic cell behavior. (C) 2014 Wiley Periodicals, Inc.