Conducting nanofibers of polyaniline (PANi) doped with camphor-10-sulfonic acid (HCSA), blended with poly(ethylene oxide) (PEO), and filled with 1-pyrenebutanoic acid, succinimidyl ester functionalized graphene (G-PBASE) have been fabricated using electrospinning. Scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), Fourier transforms infrared (FT-IR) and thermal gravimetric analyzer (TGA) was utilized to characterize the PANi/PEO/G-PBASE fibers morphology and properties. The observations show that electrospun fibers are highly interconnected and possess a relatively smooth surface. The average diameter of fibers was 222 +/- 60 nm. The electrical conductivity of PANi/PEO and PANi/PEO/G-PBASE at room temperature was also studied. The unique nanostructured composite of PANi/PEO/G-PBASE with small loading of G-PBASE (5 wt.% relative to PANi) showed two order of magnitude enhancement in the electrical conductivity and one order of magnitude enhancement in thermal stability in comparison to PANi/PEO nanofibers. (C)) 2014 Elsevier B.V. All rights reserved.