Rodlike polymer samples were made from three kinds of poly(ethylene terephthalate) (PET) pellets with different intrinsic viscosities (IV), and from polyalirate (Vectra) pellets. PET and Vectra fibers were produced using a melt-electrospinning system equipped with a CO(2)-laser melting device from these rodlike samples. The effects of IV value and laser output power on the fiber diameter of PET were investigated. Furthermore, the effect of the laser output power on the fiber diameter of Vectra was investigated. The crystal orientation of these produced fibers was also investigated by X-ray photographs. The following conclusions were reached: (i) the diameter of PET fiber decreases with increasing laser output power; (ii) the minimum average diameter of PET fibers is scarcely influenced by the value of IV; (iii) the electrospun PET fibers show isotropic crystal orientation; (iv) fibers having an average fiber diameter smaller than 1 mu m cannot be obtained from PET and Vectra using the system developed; and (v) preferred liquid crystal orientation can be seen in electrospun Vectra fibers. (c) 2007 Wiley Periodicals, Inc.