This paper reports the novel results of activated carbon nanofibers (ACNF) used to improve the toluene adsorption capacity. The ACNF was prepared by stabilization, carbonization and activation after electrospinning the polymer solution of polyacrylonitrile (PAN) in N, N-dimethylformamide. The average diameter of the ACNF was approximately 300 nm, ranging from 200 to 500 nm. The toluene adsorption capacity of ACNF10 activated at 1000 degrees C increased to 65 g-toluene/100 g-ACNF. This was attributed to the high specific surface area (1403 m(2)/g), large micropore volume (0.505 cm(3)/g), and narrow average pore diameter (6.0 angstrom). The oxygen to carbon ratio (O/C ratio) in ACNF10 was 1.8%. This O/C ratio appears to induce a higher toluene adsorption capacity, which originates from a non-polar interaction between the ACNF surface and toluene. in conclusion, the electrospun ACNF prepared in this study promotes the adsorption of toluene through the high specific surface area, large pore volume, narrow pore diameter and low O/C ratio. (C) 2008 Elsevier B.V. All rights reserved.